Retouching putty Metal epoxy stick

Article No. 0893449011
Retouching putty epoxi-stick metal high temperatur RETCHPUTY-(EPOXI STICK)-ME-120G
€17.70 inc. VAT price per 1 PCS
AVAILABLE
*
+ -
2-component compound for quick and simple repairs of surface damage.

Easy to use

  • Time-consuming mixing no longer required
  • Good dispensing facility
  • Quick to apply

Excellent adhesion properties

  • High-strength
  • Numerous application options

Simple to process further

  • Suitable for a wide range of post-processing options, such as drilling, milling, sawing and sanding
  • Can be painted over

High degree of temperature resistance

Temperature resistance up to 120°C, briefly up to 150°C

Notice

Protect from frost and direct sunlight when not applied. Gloves should be worn when applying the repair compound. Due to the different material densities, there are differences in the information regarding the weight of each stick type. For applications subject to high material stresses, the suitability of the repair compound must be checked with preliminary testing.

The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.

2-component compound for quick and simple repairs of surface damage.

Easy to use

  • Time-consuming mixing no longer required
  • Good dispensing facility
  • Quick to apply

Excellent adhesion properties

  • High-strength
  • Numerous application options

Simple to process further

  • Suitable for a wide range of post-processing options, such as drilling, milling, sawing and sanding
  • Can be painted over

High degree of temperature resistance

Temperature resistance up to 120°C, briefly up to 150°C

Notice

Protect from frost and direct sunlight when not applied. Gloves should be worn when applying the repair compound. Due to the different material densities, there are differences in the information regarding the weight of each stick type. For applications subject to high material stresses, the suitability of the repair compound must be checked with preliminary testing.

The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.

Application area

For filling surface damage to metal, e.g. gear unit housing, aluminium and die-cast parts etc.


Application substrates: Steel (plain and anodised), zinc sheets, cast iron, aluminium, copper, brass, chrome, titanium, lead and stainless steel

Instructions

1. The surface must be clean, free from grease and load-bearing. Roughening the surface beforehand improves adhesiveness


2. Twist off or cut off the required quantity and knead with your fingers until an even colour is achieved


3. Then apply the repair compound within the next 2–3 minutes


4. Dampen your hands with water to improve the modelling process


5. After another approx. 20 minutes, the compound is completely hardened and can be processed further

Products specifications
Chemical basis Epoxy resin
Colour Silver coloured
Density 1.85 g/cm³
Length 175 mm
Diameter (Ø) 22 mm
Can be further processed after min. 20 min
Processing time 3 min
Min. final strength 3 h
Conditions for final strength at 23°C
Min. processing temperature 5 °C
Max. processing temperature 25 °C
Min. temperature conditions -20 °C
Max. temperature conditions 120 °C
Max. short-term temperature resistance 150 °C
Min. temperature resistance of the hardened material -20 °C
Max. temperature resistance of the hardened material 120 °C
Substrates with good adhesion Copper<br>Brass<br>Aluminium<br>Lead<br>Chrome<br>Stainless steel<br>Cast iron<br>Steel (bare and anodised)<br>Titanium<br>Zinc sheets
Shore D hardness 87
Min. tensile strength 6.4 N/mm²
Shelf life from production 24 Month
Conditions to maintain shelf life from production frost-free storage area, no exposure to sunlight

Würth Catalogue(2)

Catalogue page as PDF 1

Flip catalog

Datasheets(1)

Safety data sheet 1

Certificates/Documents(1)

Technical data sheet 1

Products specifications
Chemical basis Epoxy resin
Colour Silver coloured
Density 1.85 g/cm³
Length 175 mm
Diameter (Ø) 22 mm
Can be further processed after min. 20 min
Processing time 3 min
Min. final strength 3 h
Conditions for final strength at 23°C
Min. processing temperature 5 °C
Max. processing temperature 25 °C
Min. temperature conditions -20 °C
Max. temperature conditions 120 °C
Max. short-term temperature resistance 150 °C
Min. temperature resistance of the hardened material -20 °C
Max. temperature resistance of the hardened material 120 °C
Substrates with good adhesion Copper<br>Brass<br>Aluminium<br>Lead<br>Chrome<br>Stainless steel<br>Cast iron<br>Steel (bare and anodised)<br>Titanium<br>Zinc sheets
Shore D hardness 87
Min. tensile strength 6.4 N/mm²
Shelf life from production 24 Month
Conditions to maintain shelf life from production frost-free storage area, no exposure to sunlight