• AOX-free
• Yes

• Chemical basis
• Acrylic resin
• Modified alkyd resin

• Coating thickness
• 40 µm

• Colour
• Zinc
• Zinc, bright

• Conditions for dust-drying time
• at recommended dry layer thickness

• Conditions for resistance in salt-spray test
• in accordance with DIN 50021

• Conditions to maintain shelf life from production
• at 10°C to 25°C

• Contents
• 400 ml

• Cross-cut test
• MAN 0-1

• Cross-cut test conditions
• in accordance with DIN 53151

• Dry layer thickness (first back-and-forth motion)
• 40 µm

• Dust-drying time
• 15 min
• 5 min

• Fully hardening/curing conditions
• At recommended dry layer thickness

• Gloss level
• Glossy
• Matt

• Grip strength conditions
• at recommended dry layer thickness

• Max. curing time
• 12 h

• Max. grip strength
• 20 min

• Min. curing time
• 1 h
• 10 h

• Min. flashing point
• 21 °C
• -42 °C

• Min. grip strength
• 15 min

• Min./max. grip strength
• 15-20 min

• Purity rating zinc
• 99 %
• 99.99 %

• Recoatable/Can be painted over
• Conditional, preliminary testing required

• Resistance in salt-spray test
• 250 h
• 500 h

• Shelf life from production
• 24 Month

• Spot weldable
• Yes

• Substrates with good adhesion
• Ferrous metals<br>PMMA<br>Polycarbonate<br>Polystyrene<br>Galvanised surfaces
• Steel<br>Zinc plated steel

• Max. temperature resistance
• 240 °C
• 400 °C