• Building material class
• B2 - Normally inflammable

• Chemical basis
• Acetate-curing sealant
• Dimethacrylic acid ester
• Epoxy resin
• Methacrylic acid ether
• Polyurethane
• Water glass luting with mineral fillers
• Neutral crosslinked silicones, oxime-based
• Sauer silicones (acetate systems)

• Chemical basis
• Methacrylate

• Colour
• Black
• Cast grey
• Orange fluorescent
• Red brown
• Violet
• Yellow fluorescent
• Grey
• White
• Red

• Conditions to maintain shelf life from production
• at max. 25°C
• cool and dry storage area below 25°C
• in sealed cartridge, max. 30°C

• Container
• Cartridge

• Contents
• 200 ml
• 44 ml
• 44.4 ml
• 70 ml
• 310 ml

• Density
• 1.05 g/cm³
• 1.08 g/cm³
• 1.12 g/cm³
• 1.25 g/cm³
• 2.21 g/cm³
• 1 g/cm³
• 1.2 g/cm³

• Density conditions
• at 25°C
• at 20°C

• Density/conditions
• 1.05 g/cm³ / at 20°C

• Dielectric strength
• 16 kV/mm

• Full curing speed
• 1 mm/d
• 1.5 mm/d
• 3 mm/d

• Fully hardening/curing conditions
• 23°C and 50% relative humidity

• Min. flashing point
• 250 °C
• 90 °C
• 100 °C

• Min. skin-formation time
• 5 min
• 6 min
• 8 min

• Min./max. temperature conditions
• -55 to 150 °C

• Min./max. temperature resistance
• -5 to 1000 °C
• -50 to 250 °C
• -50 to 280 °C
• -55 to 150 °C
• -60 to 260 °C
• -60 to 315 °C

• Product weight (per item)
• 74 g
• 76 g

• Recoatable/Can be painted over
• No

• Shelf life from production
• 24 Month
• 12 Month
• 60 Month
• 18 Month

• Shelf life from production/conditions
• 12 Month / at room temperature

• Shore A hardness
• 26
• 30
• 25

• Silicone-free
• Yes

• Smell/fragrance
• Mild
• Neutral
• Vinegar
• Characteristic

• Ultraviolet resistance
• Yes

• Weight of content
• 100 g
• 50 g
• 89.6 g

• Colour
• Yellow fluorescent

• Viscosity/consistency
• Pasty

• Density
• 1.09 g/cm³

• Fungicidal properties
• No

• Heat conductance λ
• 0.2 J/(m*s*K)

• Range of applications
• Oil pumps<br>Front cover<br>Camshaft bearing cover<br>Oil pans<br>Transmission cover<br>Exhaust manifold<br>Exhaust flange<br>Cover and flange on engines<br>Intake area
• Water pumps<br>Oil pumps<br>Front cover<br>Camshaft bearing cover<br>Thermostat housing<br>Oil pans<br>Transmission cover<br>Intake area<br>Sealing of accumolators
• Water pumps<br>Oil pumps<br>Front cover<br>Camshaft bearing cover<br>Thermostat housing<br>Oil pans<br>Transmission cover<br>Sunroof<br>Doors

• Heat conductance λ conditions
• in accordance with ASTM D-2214/70

• Max. short-term temperature resistance
• 300 °C
• 370 °C

• Min./max. viscosity 1
• 100000-180000 mPas

• Min./max. viscosity 1
• 20.000-40.000 mPas

• Conditions for viscosity 1
• at 25°C, Brookfield RVT, spindle 6/2.5 rpm

• Max. change in volume
• 25 %

• Max. gap-filling ability
• 0.35 mm

• Min./max. skin-formation time
• 5-7 min
• 8-12 min

• Max. pressure
• 690 bar

• Min./max. initial strength
• 5-15 min

• Min./max. tensile strength /conditions
• 8-10 N/mm² / in accordance with ASTM D-2095

• Min./max. viscosity 2
• 30000-40000 mPas

• Min./max. working life
• 5-7 min

• Conditions for viscosity 2
• at 25°C, Brookfield RVT, spindle 6/2.0 rpm

• Continuous motion absorption
• 20 %

• Min./max. final strength
• 12 h-24 h

• Long-term elasticity
• Virtually no elasticity

• Max. gap-filling ability
• 0.15 mm
• 0.50 mm

• Min./max. functional strength
• 3-6 h

• Min./max. processing temperature
• 5 to 30 °C
• 5 to 35 °C
• 5 to 40 °C

• Water-soluble
• Not readily soluble in water

• Max. skin-formation time
• 12 min

• Min./max. breakaway torque
• 10-20 Nm
• 17-22 Nm
• 2-3 Nm
• 4-8 Nm

• Min./max. breakaway torque
• 25-35 Nm

• Min./max. viscosity /conditions
• 14000-20000 mPas / at 25°C, Brookfield RVT, spindle 5/2.5 rpm

• Shrinkage
• Minimal

• Breakaway torque conditions
• M10 mm

• Conditions for skin-formation time
• at 23°C and 50% relative humidity

• Elongation at break
• 300 %

• Min. breaking elongation
• 350 %

• Min./max. initial strength
• 10-20 min
• 15-30 min
• 30-40 min

• Min./max. processing temperature
• 5 to 35 °C

• Min./max prevail torque
• 10-15 Nm
• 1-2 Nm
• 1-3 Nm
• 13-17 Nm

• Min./max. final strength
• 12 h-24 h
• 3-6 h
• 6-24 h

• Shelf life from production
• 24 Month

• Suitable for
• Thread diameter max. M80<br>Thread diameter max. R 3 inch
• Thread diameter max. R 3 inch (M80)
• Thread diameter max. R 3/4 inch

• Viscosity conditions
• at 25°C, Brookfield RVT, spindle 5/2.5 rpm

• Conditions for prevail torque
• M10

• Min./max. functional strength
• 1-3 h
• 2-3 h
• 3-6 h

• Nominal diameter
• 80 mm

• Shelf life from production/conditions
• 24 Month / cool and frost-free storage area, in sealed original container

• Coefficient of thermal expansion
• 0.0002 1/K

• Conditions for tensile strength
• in accordance with ASTM D-412

• Continuous motion absorption (up to 150°C)
• 25 %

• Min. tensile strength
• 2.2 N/mm²

• Min./max. compressive shearing strength
• 1-3 N/mm²
• 2-6 N/mm²
• 6-13 N/mm²

• Min./max. compressive shearing strength /conditions
• 5-10 N/mm² / in accordance with DIN 54452

• Continuous motion absorption (above 150°C)
• 18 %

• Resistance against
• Aging
• Fats<br>Household cleaning products<br>Oil<br>Flue gases and their condensates

• Max. breaking elongation/conditions
• 500 % / in accordance with DIN 53504
• 550 % / in accordance with DIN 53504

• Conditions for specific volume resistivity
• in accordance with ASTM D-257

• Min./max. shear strength
• 5-10 N/mm²

• Conditions for tensile shear strength
• in accordance with ASTM D-950

• Surface pre-treatment required
• On porous surfaces

• Coefficient of thermal expansion conditions
• in accordance with ASTM EB-31

• Solvent-free
• Yes

• Coating compatibility
• Yes

• Dielectric strength conditions
• in accordance with ASTM D-149

• Relative permittivity
• 2.8

• Conditions for relative permittivity
• 1 MHz, ASTM D-150

• Loss factor
• 0.002

• Loss factor conditions
• 1 MHz, ASTM D-150

• Specific volume resistivity
• 1000000000000000 Ohm/cm